TI  - Evaluation of shear bond strength and SEM observation of all-in-one self-etching 
      primer used for bonding of fissure sealants.
PG  - 9-16
AB  - OBJECTIVES: To evaluate and compare enamel shear bond strength of an all-in-one 
      self-etching primer (Prompt L-Pop) to regular acid etch material when bonded to 
      two-fissure sealant systems (Concise and Dyract Seal). METHOD AND MATERIALS: 
      Forty newly extracted non-carious first permanent molars were embedded in a 
      Teflon mold. The teeth were divided into four groups and each consisted of ten 
      specimens. The bonding surfaces were treated with either Prompt L-Pop as 
      recommended by the manufacturer or etched with phosphoric acid. After 24 hours of 
      water storage, the specimens were evaluated for shear bond strength using an 
      Instron testing machine. Scanning electron microscope (SEM) examinations were 
      carried out to evaluate the failure sites of the sealants. RESULTS: The mean 
      shear bond strengths using Prompt L-Pop were Concise: 23.46 MPa and Dyract Seal: 
      20.34 MPa. These values were higher than and statistically different from those 
      of Dyract Seal (9.99 MPa) and Concise (8.85 MPa) when phosphoric acid was used. 
      The failure was predominantly of the adhesive type. The SEM examination showed 
      the failure of debonding was predominantly related to the type of etching systems 
      used rather than the type of fissure sealants. CONCLUSION: The use of the 
      all-in-one self-etching adhesive Prompt L-Pop improves the mean enamel shear bond 
      strength of fissure sealants.
FAU - Al-Sarheed, Maha Abdulla
AU  - Al-Sarheed MA
AD  - Division of Pediatric Dentistry, Department of Preventive Dental Science, College 
      of Dentistry, King Saud University, Riyadh, Saudi Arabia. alsarheedm@yahoo.com
LA  - eng
PT  - Comparative Study
PT  - Journal Article
DEP - 20060501
PL  - India
TA  - J Contemp Dent Pract
JT  - The journal of contemporary dental practice
JID - 101090552
RN  - 0 (Compomers)
RN  - 0 (Phosphoric Acids)
RN  - 0 (Pit and Fissure Sealants)
RN  - 0 (Prompt L-Pop)
RN  - 0 (Resin Cements)
RN  - 0 (dyract seal)
RN  - 454I75YXY0 (Bisphenol A-Glycidyl Methacrylate)
RN  - E4GA8884NN (phosphoric acid)
SB  - IM
MH  - Acid Etching, Dental/*methods
MH  - Analysis of Variance
MH  - Bisphenol A-Glycidyl Methacrylate
MH  - Compomers
MH  - *Dental Bonding
MH  - Dental Stress Analysis
MH  - Humans
MH  - Materials Testing
MH  - Microscopy, Electron, Scanning
MH  - Molar
MH  - Phosphoric Acids
MH  - *Pit and Fissure Sealants
MH  - *Resin Cements
MH  - Shear Strength
EDAT- 2006/05/11 09:00
MHDA- 2006/06/13 09:00
CRDT- 2006/05/11 09:00
PHST- 2006/05/11 09:00 [pubmed]
PHST- 2006/06/13 09:00 [medline]
PHST- 2006/05/11 09:00 [entrez]
AID - 1526-3711-298 [pii]
PST - epublish
SO  - J Contemp Dent Pract. 2006 May 1;7(2):9-16.