AB  - Hydrocarbonate-gel method was applied to prepare MgSrAl10O17:Eu2+ blue phosphors 
      with quasi-spherical morphology. Scanning electron microscope (SEM) and powder 
      X-ray diffraction (XRD) were employed to characterize the resulting products. SEM 
      image showed that the phosphor particles were of quasi-spherical shape with the 
      diameter in the range of 1 approximately 3 microm. X-ray diffraction patterns of 
      the resulting samples displayed pure MgSrAl10O17 phase after annealed at 1270 
      degrees C for 3 h. The effects of annealing temperature, parameters on 
      crystalline phase evolution and photoluminescence intensities of the resulting 
      phosphor were also studied. Upon excitation with UV irradiation, MgSrAl10O17:Eu2+ 
      shows a strong blue emission at 468 nm corresponding to 4f65d1 --> S7/2 
      transition of Eu2+, which has potential applications in fluorescent lamps and 
      plasma display panels.
FAU - Wang, Jinghui
AU  - Wang J
AD  - State Key Laboratory of Fine Chemicals and School of Chemical Engineering, Dalian 
      University of Technology, Dalian 116012, PR China.
FAU - Ye, Junwei
AU  - Ye J
FAU - Pang, Hongchang
AU  - Pang H
FAU - Lin, Yuan
AU  - Lin Y
FAU - Ning, Guiling
AU  - Ning G
LA  - eng
PT  - Journal Article
PT  - Research Support, Non-U.S. Gov't
PL  - United States
TA  - J Nanosci Nanotechnol
JT  - Journal of nanoscience and nanotechnology
JID - 101088195
EDAT- 2009/11/17 06:00
MHDA- 2009/11/17 06:01
CRDT- 2009/11/14 06:00
PHST- 2009/11/14 06:00 [entrez]
PHST- 2009/11/17 06:00 [pubmed]
PHST- 2009/11/17 06:01 [medline]
AID - 10.1166/jnn.2009.1782 [doi]
PST - ppublish
SO  - J Nanosci Nanotechnol. 2009 Dec;9(12):7496-8. doi: 10.1166/jnn.2009.1782.