TI  - Monomer Release from Resin Based Dental Materials Cured With LED and Halogen 
      Lights.
PG  - 34-40
AB  - OBJECTIVES: To measure the release of TEGDMA and BisGMA from two commercially 
      available composite resins; Filtek Z 250 (3M ESPE, Germany), Leaddent (Leaddent, 
      Germany) and two fissure sealants; Helioseal F (3M ESPE, Germany) Enamel Loc 
      (Premiere Rev, USA) over 1, 3 and 7 days after polymerization with standard 
      quartz-tungsten halogen Coltolux II (QHL) (Coltene Switzerland) and a standard 
      blue light emitting diode Elipar Freelight 2 (3M ESPE, Germany). METHODS: 9 
      samples of each material were placed in disc shaped specimens in 1 mm of 
      thickness and 10 mm in diameter (n=36). Each material was polymerized using LED 
      for 20 s (n=12), 40 s (n=12) and halogen for 40 s (n=12), respectively. High 
      Performance Liquid Chromatography (HPLC) was used to measure the amount of 
      monomers released over 1, 3 and 7 days. Data was analyzed using one way ANOVA and 
      Bonferroni test for multiple comparisons with a significance level of .05. 
      RESULTS: LED 20 sec group showed the highest release of monomers at 1, 3 and 7 
      days in sealant groups. Halogen 40 sec group resulted highest release of monomers 
      for Leaddent at all time intervals (P<.05) CONCLUSIONS: Efficiency of the curing 
      unit and applying the recommended curing time of the light activated resin based 
      dental materials is very important to protect the patient from potential hazards 
      of residual monomers.
FAU - Ak, Asli Topaloglu
AU  - Ak AT
AD  - Research Assistant, Ege University, School of Dentistry, Department of Paediatric 
      Dentistry, Izmir, Turkey.
FAU - Alpoz, A Riza
AU  - Alpoz AR
FAU - Bayraktar, Oguz
AU  - Bayraktar O
FAU - Ertugrul, Fahinur
AU  - Ertugrul F
LA  - eng
PT  - Journal Article
PL  - Germany
TA  - Eur J Dent
JT  - European journal of dentistry
JID - 101303672
PMC - PMC2798788
OTO - NOTNLM
OT  - BisGMA
OT  - Composite resin
OT  - Fissure sealant
OT  - Residual monomer
OT  - TEGDMA
EDAT- 2010/01/05 06:00
MHDA- 2010/01/05 06:01
PMCR- 2010/01/01
CRDT- 2010/01/05 06:00
PHST- 2010/01/05 06:00 [entrez]
PHST- 2010/01/05 06:00 [pubmed]
PHST- 2010/01/05 06:01 [medline]
PHST- 2010/01/01 00:00 [pmc-release]
AID - dent04_p0034 [pii]
PST - ppublish
SO  - Eur J Dent. 2010 Jan;4(1):34-40.