TI  - [Determination of solubility parameters of high density polyethylene by inverse 
      gas chromatography].
PG  - 1118-21
AB  - Inverse gas chromatographic (IGC) technology was used to determine the solubility 
      parameters of high density polyethylene (HDPE) at the absolute temperatures from 
      303.15 to 343.15 K. Six solvents were applied as test probes including hexane 
      (n-C6), heptane (n-C7), octane (n-C8), nonane (n-C9), chloroform (CHCl3) and 
      ethyl acetate (EtAc). Some thermodynamic parameters were obtained by IGC data 
      analysis such as the specific retention volumes of the solvents (V(0)(g)), the 
      molar enthalpy of sorption (delta H(S)(1)), the partial molar enthalpy of mixing 
      at infinite dilution (delta H(1)(infinity)), the molar enthalpy of vaporization 
      (delta H(v)), the activity coefficients at infinite dilution (omega 
      (1)(infinity)), and Flow-Huggins interaction parameters (X(1,2)(infinity)) 
      between HDPE and probe solvents. The results showed that the above six probes are 
      poor solvents for HDPE. The solubility parameter of HDPE at room temperature 
      (298.15 K) was also derived as 19.00 (J/cm3)(0.5).
FAU - Wang, Qiang
AU  - Wang Q
AD  - Center for Physics and Chemistry Analysis, Xinjiang University, Urumqi 830046, 
      China.
FAU - Chen, Yali
AU  - Chen Y
FAU - Liu, Ruiting
AU  - Liu R
FAU - Shi, Yuge
AU  - Shi Y
FAU - Zhang, Zhengfang
AU  - Zhang Z
FAU - Tang, Jun
AU  - Tang J
LA  - chi
PT  - English Abstract
PT  - Journal Article
PL  - China
TA  - Se Pu
JT  - Se pu = Chinese journal of chromatography
JID - 9424804
EDAT- 2012/03/08 06:00
MHDA- 2012/03/08 06:01
CRDT- 2012/03/08 06:00
PHST- 2012/03/08 06:00 [entrez]
PHST- 2012/03/08 06:00 [pubmed]
PHST- 2012/03/08 06:01 [medline]
PST - ppublish
SO  - Se Pu. 2011 Nov;29(11):1118-21.